Blend of a polyester and a polycarbonate

ABSTRACT

A polymeric blend comprising a polyester and a polycarbonate, wherein: the polyester contains recurring units having the structure &lt;IMAGE&gt;   and the polycarbonate contains recurring units having the structure   &lt;IMAGE&gt;

FIELD OF THE INVENTION

This invention relates to a blend of a polyester and a polycarbonate and, more particularly, to such a blend wherein the polyester and the polycarbonate are very compatible; i.e., the polyester and the polycarbonate can form a solid solution with each other.

BACKGROUND

Bisphenol A polycarbonate is a well known and widely used engineering thermoplastic having utility for producing molded articles and protective plastic overcoats. It is known to exhibit good hardness, good impact resistance, and, in its amorphous higher molecular weight forms, good transparency. However, bisphenol A polycarbonate has drawbacks for some applications, namely, lower than desirable glass transition temperature (Tg), poor resistance to stress cracking caused by contact with solvents such as gasoline or other chemicals, and, in its lower molecular weight forms, a tendency to crystallize and thereby become hazy rather than transparent.

In contrast, some thermoplastic polyesters, while not having as high impact resistance as bisphenol A polycarbonate, have higher Tg, excellent resistance to stress cracking caused by contact with solvents or other chemicals, and good amorphousness and transparency over a wider range of molecular weights.

It would be desirable to be able to provide a polymeric composition, for example by blending a polyester with bisphenol A polycarbonate, that would provide a combination of the beneficial properties of both the polyester and bisphenol A polycarbonate, e.g., good hardness, high impact resistance, high transparency, high Tg, good resistance to chemical-caused stress cracking, and relatively reasonable cost. Unfortunately, these goals have been thwarted in the past by the inherent incompatibilities of many polyesters with bisphenol A polycarbonate. By "incompatibility", we mean the inability of the two polymers to form and/or maintain a solid solution with each other over a wide range of proportions and external conditions. Incompatibility of a blend of two or more polymers is evidenced by the blend's having more than one Tg, which is a reliable indicator that the polymers in the blend exist in separate phases, each exhibiting properties different from each other, rather than the single set of properties exhibited by a blend of compatible polymers that form a solid solution with each other, i.e., form a single phase in the blend. Inherent drawbacks of phase separations between the polymers in a blend include: inability to provide a higher single Tg, poorer structural integrity, poorer resistance to impact and other stress, poorer resistance to cracking caused by chemical attack, and poorer transparency due to light scattering, all of which are contrary to the purposes intended in creating the blend.

Thus, a need exists for a blend of a polyester and bisphenol A polycarbonate, wherein the blended polymers are compatible with each other over a wide range of proportions, and wherein the blend exhibits good amorphousness and transparency, good impact resistance, a single Tg higher than that of the bisphenol A polycarbonate itself, better resistance to chemically caused stress cracking than that of the bisphenol A polycarbonate itself, and reasonable cost.

SUMMARY OF THE INVENTION

The present invention satisfies the above-noted need by providing a polymeric blend comprising a polyester and a polycarbonate, wherein:

the polyester contains recurring units having the structure ##STR3##

and the polycarbonate contains recurring units having the structure ##STR4##

The polyester and polycarbonate in the blend of this invention are very compatible with each other; they can form a solid solution with each other when combined in any proportions. The blend exhibits a single Tg, which is higher than the Tg of bisphenol A polycarbonate itself. The blend exhibits good amorphousness and transparency over a wide range of molecular weights of both polymers in the blend, good impact resistance, and better resistance to chemically caused stress cracking than that of bisphenol A polycarbonate itself. The blend can be obtained at reasonable cost, and has utility for producing molded or cast articles and protective overcoats.

DESCRIPTION OF PREFERRED EMBODIMENTS

The polymers having recurring units of Structure (II) employed in the blends of this invention are well known bisphenol A polycarbonates and can be prepared by any of the methods well known in the art for synthesizing such polycarbonates. Bisphenol A polycarbonates having weight average molecular weights within the range of from 10,000 to 200,000 are useful in accordance with the invention.

The polymers having recurring units of Structure (I) employed in the blends of this invention are polyesters and can be prepared by methods generally known to be useful for polyester syntheses, e.g., by condensation of appropriate diacids (or their esters or salts) with appropriate diols. For example, an appropriate diacid salt is 2,5-dimethylterephthaloyl chloride, which can be prepared by condensation of thionyl chloride with the diacid, 2,5-dimethylterephthalic acid, which is readily commercially available, e.g., from the Bader subsidiary of the Aldrich Chemical Co., USA or from Chem Service, Inc., West Chester, PA, USA. An appropriate diol is tetramethylbisphenol A, which can be prepared by condensation of 2,6-dimethylphenol with acetone. Further details of preparations of the diacid salt, the diol, and the polyester are presented in Preparations 1-3, below. Polyesters having recurring units of Structure (I), that are useful in accordance with the invention, have weight average molecular weights within the range of from 10,000 to 200,000.

Blends in accordance with the invention contain the polyester and the polycarbonate in any desired proportions, so long as each is present in greater than zero amount. The particular proportions chosen will depend upon the particular balance of properties desired. However, whatever proportions are chosen, it has been unexpectedly found that the polycarbonate having recurring units of Structure (II) is fully compatible with the polyester having recurring units of Structure (I); i.e., the polyester and polycarbonate can be blended in any proportions to form a solid solution having a single phase and a single Tg.

Blends of this invention can be formed by any means well known in the art for preparing a solid solution of different polymers. For example, the polymers can be dissolved and well-mixed in any solvent in which both polymers are fully soluble (e.g., dichloromethane) followed by drying off the solvent (to produce the blend in bulk), or mixing the solution with a liquid in which the polymers are not soluble (to precipitate the blend in particulate form), or followed by solvent-coating a layer of the solution onto a substrate and then drying off the solvent to form an overcoat film of the blend on the substrate, which can remain on the substrate as a permanent overcoat or be peeled off the substrate to form a free-standing film. Alternatively, for example, the polymers can be physically melt-blended in any suitable device (e.g., an extruder) at a temperature high enough to allow easy flow and thorough mixing of both polymers, followed by cooling in bulk or chopped pellet form or melt-coating a layer or molding into a desired shape and then cooling. The method of blending is not critical, so long as it enables thorough mixing and the formation of a solid solution.

The following preparations and examples are presented to further illustrate some blends in accordance with the invention and to compare their properties to those of blends or single polymers outside the scope of the invention.

A polyester containing recurring units having Structure (I) was synthesized as described in Preparations 1-3, below.

PREPARATION 1 2,5-Dimethylterephthaloyl chloride

In a 2-liter 3-necked round-bottom flask, equipped with a stirrer, condenser, and nitrogen gas inlet, was placed 171 g (0.88 mol) of 2,5-dimethylterephthalic acid, 500 g of thionyl chloride, and 5 ml of dimethyl formamide. The mixture was heated to reflux under nitrogen until the solution became clear (about 18 hours). The excess thionyl chloride was evaporated under reduced pressure. The residue was taken up in hot hexane which was then removed under reduced pressure. The residue was recrystallized from hot hexane to obtain 156 g (77%) of shiny white crystals of the desired product, 2,5-dimethylterephthaloyl chloride.

PREPARATION 2 Tetramethylbisphenol A

In a 1-liter 3-necked round-bottom flask equipped with a condenser, stirrer and HCl gas inlet tube, were placed 244 g (2.0 mol) of 2,6-dimethylphenol and 116 g (2.0 mol) of reagent grade acetone. HCl gas was then bubbled into the reaction mixture for approximately 5 hours (i.e., until the mixture was saturated with HCl). The reaction mixture was stirred at room temperature for 24 hours, and the solids were filtered and washed twice with 1 liter of hexanes, followed by 1 liter of distilled water, then again with hexanes. The crude product was recrystallized from 1.5 liters of 80% aqueous methanol, collected, and dried in a vacuum oven at 50° C. for 24 hours to give 185 g (65%) of the desired product as white crystals.

Melting point=164° C.

Elemental Analysis: calculated for C₁₉ H₂₄ O₂ : 80.2% C, 8.5% H, found: 80.2% C, 8.5% H.

PREPARATION 3 Poly(tetramethylbisphenol A 2,5-dimethylterephthalate), Structure (I)

To a stirred mixture of tetramethylbisphenol A (28.44 g, 0.10 mol) and triethylamine (22.3g, 0.22 mol) in methylene chloride (100 ml) at 10° C. was added a solution of 2,.5-dimethylterephthaloyl chloride (23.4 g, 0.10 mol) in methylene chloride (70 ml). After addition, the temperature was allowed to rise to room temperature, and the solution was stirred under nitrogen for 4 hours, during which triethylamine hydrochloride precipitated in a gelatinous form and the solution became viscous. The solution was then filtered and washed with dilute hydrochloric acid, 2% (100 ml) followed by water (3×200 ml). The solution was then poured into methanol with vigorous stirring, and a white fibrous polymer, the desired product, precipitated. The isolated polymer was dried in a vacuum oven at 40° C. for 24 hours.

Weight average molecular weight=27,100.

Number average molecular weight=12,300.

(Molecular weights were determined by gel permeation chromatography based on polystyrene equivalents.)

Glass transition temperature (by differential scanning calorimetry)=170° C.

EXAMPLES 1-3

Blends in accordance with the invention were prepared by thoroughly dissolving and mixing in dichloromethane various proportions of bisphenol A polycarbonate, Structure (II) (sold under the trademark, Makrolon 5700, by Mobay Chemical Co., USA and having a weight average molecular weight of 175,000 and a number average molecular weight of 34,000), and the polyester of Structure (I) (prepared in accordance with Preparations 1-3, above), solvent casting the various solutions, and then drying off the solvent to yield free-standing films of the blends.

Each of the blends of Examples 1-3 exhibited good amorphousness and transparency, good impact resistance, better resistance to chemically caused stress cracking than that of the bisphenol A polycarbonate itself, and a single Tg (determined by differential scanning calorimetry) higher than the Tg of the bisphenol A polycarbonate itself.

For purposes of comparison, control films outside the scope of the invention were prepared as in Examples 1-3, except that Control A was composed of 100% of the Makrolon bisphenol A polycarbonate, Control B was composed of 100% of the Structure (I) polyester, and Control C was composed of a 50:50 weight ratio blend (disclosed in U.S. Pat. No. 4,840,861) of the Makrolon bisphenol A polycarbonate and a polyester formed from 2,2-bis(4-hydroxyphenyl)propane and terephthalic:isophthalic acids (55:45 molar ratio) (a polyester sold under the trademark, Ardel D-100, by Amoco, Inc., USA). The Control C film had a hazy visual appearance (i.e., poor transparency) and exhibited two separate Tg's (determined by differential scanning calorimetry), which indicates that the polymers in the blend were incompatible and formed separate phases.

Relevant data is presented in Table I, below.

                  TABLE I                                                          ______________________________________                                                    Weight Ratio     Tg('s)                                             Example    (polyester:polycarbonate)                                                                       (°C.)                                       ______________________________________                                         Control A   0:100           154                                                1          25:75            162                                                2          50:50            167                                                3          75:25            168                                                Control B  100:0            170                                                Control C  50:50            155 and 191                                        ______________________________________                                    

EXAMPLES 4-8

Blends in accordance with the invention were prepared by thoroughly dissolving and mixing in dichloromethane various proportions of bisphenol A polycarbonate, Structure (II) (sold under the trademark, Makrolon 5700, by Mobay Chemical Co., USA), and the polyester of Structure (I) (prepared in a manner similar to Preparations 1-3, above, except that the resultant polymer was determined to have a weight average molecular weight of 27,300, a number average molecular weight of 11,500, and a Tg of 176° C.), solvent casting the various solutions, and then drying off the solvent to yield free-standing films of the blends.

Each of the blends of Examples 4-8 exhibited good amorphousness and transparency, good impact resistance, better resistance to chemically caused stress cracking than that of the bisphenol A polycarbonate itself, and a single Tg (determined by differential scanning calorimetry) higher than the Tg of the bisphenol A polycarbonate itself.

For purposes of comparison, control films outside the scope of the invention were prepared as in Examples 4-8, except that Control D was composed of 100% of the Makrolon bisphenol A polycarbonate, Control E was composed of 100% of the Structure (I) polyester, and Control F was composed of a 50:50 weight ratio blend (disclosed in U.S. Pat. No. 4,840,861) of the Makrolon bisphenol A polycarbonate and a polyester formed from 2,2-bis(4-hydroxyphenyl)propane and terephthalic:isophthalic acids (55:45 molar ratio) (a polyester sold under the trademark, Ardel D-100, by Amoco, Inc., USA). The Control F film had a hazy visual appearance (i.e., poor transparency) and exhibited two separate Tg's (determined by differential scanning calorimetry), which indicates that the polymers in the blend were incompatible and formed separate phases.

Relevant data is presented in Table II, below.

                  TABLE II                                                         ______________________________________                                                    Weight Ratio     Tg('s)                                             Example    (polyester:polycarbonate)                                                                       (°C.)                                       ______________________________________                                         Control D   0:100           155                                                4          10:90            158                                                5          30:70            163                                                6          50:50            169                                                7          70:30            172                                                8          90:10            173                                                Control E  100:0            176                                                Control F  50:50            152 and 187                                        ______________________________________                                    

The invention has been described in detail with particular reference to certain preferred embodiments thereof, but it should be appreciated that variations and modifications can be effected within the spirit and scope of the invention. 

What is claimed is:
 1. A polymeric blend comprising a polyester and a polycarbonate, wherein:the polyester contains recurring units having the structure ##STR5## and the polycarbonate contains recurring units having the structure ##STR6##
 2. The polymeric blend of claim 1, wherein the polyester has a weight average molecular weight of from 10,000 to 200,000, and the polycarbonate has a weight average molecular weight of from 10,000 to 200,000.
 3. The polymeric blend of claim 1, having only a single glass transition temperature, that temperature being greater than 154° C. 